PENGARUH VARIASI PERMUKAAN CONE TERHADAP INTERMETALIK PADA PENGELASAN ROTARY FRICTION WELDING AL DAN CU

Hafiz Alfara; Agus Fikri;

Permukaan Cone Terhadap Intermetalik Pada Pengelasan Rotary Friction Welding Al dan Cu.

Hafiz Alfara

Telah dikembangkan proses pengelasan keadaan lumer seperti teknik rotary friction welding, upaya
ini dilakukan untuk menghindari sulitnya proses pengelasan dua material berbeda yang
mengakibatkan terjadinya keretakan panas dan porositas. Proses rotary friction welding(RFW)
merupakan teknik pengelasan material dalam kondisi lumer (tidak mencapai titik cair), Prosesnya
material dijepit agar tidak terlempar, sebuah material berputar diarahkan bertemuan material yang
disambung, dan pertemuan dua sisi material karena adanya penekanan. Tulisan ini meneliti pengaruh
variasi cone logam yang berbeda, antara paduan aluminium dan paduan tembaga terhadap sifat
intermetalik sambungan las. Parameternya adalah variasi cone 30°, 45°, 60°, waktu gesek 60 s,
waktu tekan 30 s dan kecepatan putaran mesin bubut 1000 rpm. Proses pengelasan menggunakan
mesin bubut yang dilengkapi mekanisme pembebanan hidrolik. Hasil pengujian menunjukkan
terjadi proses pengelasan pada kedua permukaan metal. Adanya percampuran kedua logam di daerah
sambungan pengelasan.

Kata kunci: friction welding, tembaga dengan alumunium, berputar, panas, penekanan, sudut

Effect of Cone Surface Variation on Intermetallic in Rotary Friction Welding of Al and Cu.

Hafiz Alfara

A molten state welding process such as rotary friction welding technique has been developed, this
effort is made to avoid the difficulty of welding two different materials which results in hot cracks
and porosity. The rotary friction welding (RFW) process is a material welding technique in the
molten state (not reaching the liquid point), the process of material is clamped so as not to be
thrown, a rotating material is directed to meet the joined material, and the meeting of the two sides
of the material due to emphasis. This paper examines the effect of different metal cone variations,
between aluminium alloys and copper alloys on the intermetallic properties of welded joints. The
parameters are cone variations of 30°, 45°, 60°, friction time of 60 s, press time of 30 s and lathe
rotation speed of 1000 rpm. The welding process uses a lathe equipped with a hydraulic loading
mechanism. The test results show that the welding process occurs on both metal surfaces. There is
mixing of the two metals in the welding joint area.

Keywords: friction welding, copper with aluminium, rotating, heat, pressing, cone