ANALISIS PENGARUH VIBRASI PADA MEJA GETAR TERHADAP TERBENTUKNYA POROSITAS PADA LAS TIG ALUMUNIUM 6061

SHIDQI MUHAMMAD MAHFUZH; Pancatatva Hesti Gunawan;

ABSTRAK

Analisis Pengaruh Vibrasi pada Meja Getar Terhadap Terbentuknya

Porositas pada Las TIG Alumunium 6061
Shidqi Muhammad Mahfuzh

Penelitian ini bertujuan untuk mengetahui pengaruh variasi frekuensi meja getar dan kecepatan
angin terhadap tingkat porositas mikro pada sambungan hasil pengelasan TIG (Tungsten Inert Gas)
aluminium 6061. Variabel bebas yang digunakan adalah frekuensi getaran meja (30 Hz, 40 Hz, dan
50 Hz) serta kecepatan angin di sekitar area pengelasan (3,6 km/h, 4,0 km/h, dan 5,0 km/h). Evaluasi
dilakukan melalui pengujian makro dan mikrostruktur menggunakan mikroskop optik untuk
mengamati jumlah serta distribusi rongga atau pori pada sambungan las. Hasil menunjukkan bahwa
frekuensi getaran meja 40 Hz menghasilkan porositas mikro terendah, yaitu 1,249%, sedangkan
pada frekuensi 30 Hz dan 50 Hz masing-masing diperoleh 5,192% dan 1,808%. Selain itu,
peningkatan kecepatan angin cenderung menyebabkan kenaikan porositas, dengan nilai tertinggi
sebesar 1,898% pada kecepatan 5,0 km/h. Temuan ini mengindikasikan bahwa getaran mekanis pada
frekuensi tertentu serta kondisi lingkungan pengelasan dapat memengaruhi kualitas struktur
sambungan las. Penelitian ini memberikan gambaran awal tentang pentingnya pengendalian getaran
dan faktor eksternal dalam upaya meminimalkan cacat pori pada pengelasan aluminium.
Kata kunci: Pengelasan TIG, Aluminium 6061, Meja Getar, Porositas Mikro, Kecepatan Angin

Analysis of the Effect of Vibration on a Vibrating Table on the Formation

of Porosity in TIG Welding of Aluminum 6061

Shidqi Muhammad Mahfuzh

This study aims to determine the effect of vibration table frequency variation on the level of
microporosity in the welded joints of TIG (Tungsten Inert Gas) aluminum 6061. The free variables
used were the frequency of table vibration (30 Hz, 40 Hz, and 50 Hz) and wind speed around the
welding area (3.6 km/h, 4.0 km/h, and 5.0 km/h). Evaluation is carried out through macro and
microstructure testing using an optical microscope to observe the number and distribution of
cavities or pores at the weld joint. The results showed that the 40 Hz table vibration frequency
resulted in the lowest microporosity, which was 1.249%, while at the 30 Hz and 50 Hz frequencies
5.192% and 1.808% were obtained, respectively. In addition, increased wind speeds tend to lead to
an increase in porosity, with a highest value of 1.898% at a speed of 5.0 km/h. These findings
indicate that mechanical vibrations at certain frequencies as well as welding environmental
conditions can affect the structural quality of weld joints. This study provides a preliminary overview
of the importance of vibration control and external factors in an effort to minimize pore defects in
aluminum welding.
Keywords: TIG Welding, Aluminum 6061, Vibrating Table, Micro Porosity, Wind Speed