ANALISIS PERBEDAAN WAKTU TEKAN PADA PROSES FRICTION ROTARY WELDING PEMBUATAN JOINT SLEVEE PADA MATERIAL BEDA JENIS ALUMINIUM DAN TEMBAGA SKRIPSI

Dwiyanto Asharul Ramadhan; Riyan Ariyansyah;

Analisis Perbedaan Waktu Tekan Pada Proses Friction Rotary Welding
Pembuatan Joint Slevee Pada Material Beda Jenis Aluminium dan Tembaga

Dengan Pengujian SEM-EDX
Dwiyanto Asharul Ramadhan

Telah dikembangkan proses pengelasan keadaan lumer seperti teknik friction welding, upaya ini
dilakukan untuk menghindari sulitnya proses pengelasan dua material berbeda yang mengakibatkan
terjadinya keretakan panas dan porositas. Proses friction welding (FRW) merupakan teknik
pengelasan material dalam kondisi lumer (tidak mencapai titik cair), Prosesnya material dijepit agar
tidak terlempar, sebuah material berputar diarahkan bertemuan material yang disambung, dan
pertemuan dua sisi material karena adanya penekanan. Tulisan ini meneliti pengaruh variasi waktu
tekan logam yang berbeda, antara paduan aluminium dan paduan tembaga terhadap sifat intermetalik
sambungan las. Parameternya adalah variasi waktu 15, 30 dan 45 detik, waktu gesek 60 s, waktu
tekan 20 s dan kecepatan putaran mesin bubut 1300 rpm. Proses pengelasan menggunakan mesin
bubut yang dilengkapi mekanisme pembebanan hidrolik. Hasil pengujian menunjukkan terjadi
proses pengelasan pada kedua permukaan metal. Adanya percampuran kedua logam di daerah
sambungan pengelasan.
Kata kunci: friction welding, tembaga dengan alumunium, berputar, panas, penekanan

Analysis of Differences in Press Time in the Friction Rotary Welding
Process for Making Joint Slevees on Different Types of Aluminum and Copper

Materials Using SEM-EDX Testing
Dwiyanto Asharul Ramadhan

A melted welding process has been developed, such as the friction welding technique, this effort was
made to avoid the difficulty of welding two different materials which results in hot cracks and
porosity. The friction welding (FRW) process is a technique for welding materials in a melted
condition (not reaching the melting point). The process is where the material is clamped so that it
does not throw, a rotating material is directed towards meeting the material being joined, and two
sides of the material meet due to pressure. This paper examines the effect of variations in pressing
times for different metals, between aluminum alloys and copper alloys, on the intermetallic
properties of welded joints. The parameters are time variations of 15, 30 and 45 seconds, friction
time 60 s, press time 20 s and lathe rotation speed 1300 rpm. The welding process uses a lathe
equipped with a hydraulic loading mechanism. The test results show that a welding process occurs
on both metal surfaces. There is a mixture of the two metals in the welding joint area.
Keywords: friction welding, copper with aluminium, rotating, heat, pressing